ARMEPOX® DTM 243 MIO
Fast‑drying epoxy coating with a thick film, specially reinforced with iron silicate (MIO) to enhance barrier protection in painting systems for new steel structures. High solids content provides versatility: it can be used as a primer, intermediate or finish coat, as well as in a single‑coat system. MIO pigments significantly improve barrier properties, and the very rapid drying allows prompt application of subsequent layers or processing.
Specific Feature
barrier properties
Product Chemistry
epoxy
Color Options
gray
Surface Type
2K primers
Gloss Level
not standardized
- Reinforced with iron silicate oxide (MIO)
- Fast drying for application of the next coat
- Fast drying for processing
- Low-temperature application
- Intended for new construction
- Solid content of the mixture: 70 ± 2%.
- Solid content of the base: 75–95%.
- Mixture density: 1.45–1.55 kg/L.
- Base viscosity: thixotropic.
- Mixture viscosity: thixotropic.
- Mixture pot life: 6 hours.
- Drying time for a 100 µm dry film thickness:
- +10 °C:
- "Touch dry": 1 hour
- "Recoat": 6–8 hours
- Minimum intercoat drying: 4 hours
- +23 °C:
- "Touch dry": 40 minutes
- "Recoat": 5 hours
- Minimum intercoat drying: 2 hours
- +35 °C:
- "Touch dry": 30 minutes
- "Recoat": 3 hours
- Minimum intercoat drying: 1 hour
- Thermal drying:
- +60 °C: 30 minutes
Full film formation: 7 days under ambient drying.
Data are given at 65 % relative humidity. Values may change with humidity variations.