ARMOPUR® TOPCOAT 161
Two‑component acrylic‑polyurethane enamel with high gloss is intended for use as a finish layer in systems with two‑component epoxy and acrylic‑polyurethane primers. It provides excellent decorative properties, durable coating and high resistance to atmospheric influences, maintaining colour and gloss over a long service life. Ideal for high‑quality painting of commercial transport — buses, trolleybuses, trams, passenger trains, truck cabins — as well as various metal structures.
Specific Feature
high weather resistance
Product Chemistry
acrylic‑polyurethane
Color Options
Color‑matched to RAL, NCS and the sample
Surface Type
2K primers
Gloss Level
high‑gloss
- Applied to a primed surface;
- Features accelerated polymerization;
- Forms an atmosphere‑resistant coating that can retain color and gloss over a long service period;
- Suitable for use as a high‑gloss topcoat in systems with epoxy and acrylic‑polyurethane primers;
- Recommended for painting vehicles, equipment, exterior surfaces of tanks, steel frames and other steel structures, and machinery;
- Forms a coating with enhanced chemical resistance.
- Solid content of the mixture: 56 ± 2%.
- Solid content of the base: 55–75%.
- Mixture density: 1.0–1.2 kg/L.
- Viscosity of the base: >180 s (DIN4).
- Viscosity of the mixture: 70–90 s (DIN4).
- Pot life of the mixture: 1.5 h.
- Drying time at a dry film thickness of 50 µm:
- +10 °C:
- Dust resistance: 30 min
- Touch dry: 6 h
- Minimum intercoat drying: 15 min
- +23 °C:
- Dust resistance: 20 min
- Touch dry: 4 h
- Minimum intercoat drying: 5–7 min
- +35 °C:
- Dust resistance: 10 min
- Touch dry: 2 h
- Minimum intercoat drying: 5 min
- Thermal drying:
- +60 °C: 30 min
Full film formation: 7 days under natural drying.
Data are given at 65 % relative humidity. Values may change with humidity variations.