ARMEPOX® PRIMER 041
Two‑component epoxy anticorrosion primer, intended for industrial use, particularly as a base underpainting for commercial vehicles, agricultural equipment, and specialized machinery. Developed for rapid subsequent application of two‑component acrylic‑polyurethane enamels, ensuring efficient project execution. The primer provides reliable protection, excellent physico‑mechanical properties and high adhesion to steel, as well as to complex substrates such as aluminum and galvanized steel, preparing the surface for a durable and high‑quality finish coating.
Specific Feature
fast overcoat
Product Chemistry
epoxy
Color Options
light gray
beige
Surface Type
steel
aluminum
galvanized steel
- Can be applied to black metal, aluminum, galvanized steel;
- Zinc phosphate is used as the anticorrosion pigment;
- For producing coatings used in various climatic zones;
- Used as a primer coating in epoxy and acrylic‑polyurethane systems;
- Used for surfaces subject to abrasion and mechanical and/or chemical exposure.
- Volume of solids (A + B)
Version 1 – 57±1 %
Version 2 – 70±3 % - Weight of solids in the base: 65–80%.
- Mixture density: 1.4–1.5 kg/L.
- Base viscosity: >180 s (DIN4).
- Mixture viscosity: 90–150 s (DIN4).
- Mixture pot life: 6 h.
- Drying time at a dry film thickness of 50 µm:
- +10 °C:
- "From dust": 2 h
- "To touch": 6 h
- Minimum intercoat drying: 40 min
- Before applying enamel: 1 h
- +23 °C:
- "From dust": 1 h
- "To touch": 4 h
- Minimum intercoat drying: 20 min
- Before applying enamel: 40 min
- +35 °C:
- "From dust": 30 min
- "To touch": 2 h
- Minimum intercoat drying: 10 min
- Before applying enamel: 20 min
- Thermal drying:
- +60 °C: 30 min
Full coating formation: 7 days under natural drying.
Data are given at 65 % relative air humidity. Changes in humidity may affect the data.