ARMOPUR® TOPCOAT 112
Two-component acrylic‑polyurethane weather‑resistant enamel. An aliphatic isocyanate is used as the hardener.
90‑95% high‑gloss.
Specific Feature
high atmospheric resistance
Product Chemistry
acrylic‑polyurethane
Color Options
colored according to RAL, NCS and sample
Surface Type
2K primers
Gloss Level
high‑gloss
- Applied to a primed surface;
- Forms an atmospheric‑resistant coating capable of retaining color and gloss over an extended service life;
- Suitable for use as a high‑gloss topcoat in systems with epoxy and acrylic‑polyurethane primers;
- Recommended for painting vehicles, equipment, external surfaces of tanks, steel frames and other steel structures, and machine equipment.
- Solid content of the mixture: 50 ± 2%.
- Solid content of the base: 50–70%.
- Mixture density: 1.0–1.2 kg/L.
- Base viscosity: 80–160 s (DIN4).
- Mixture viscosity: 40–70 s (DIN4).
- Mixture pot life: 4 h.
- Drying time for a dry film thickness of 50 µm:
- +10 °C:
- "Dust free": 30 minutes
- "Tack‑free": 5 hours
- Minimum intercoat drying: 15 minutes
- +23 °C:
- "Dust free": 20 minutes
- "Tack‑free": 3 hours
- Minimum intercoat drying: 5–7 minutes
- +35 °C:
- "Dust free": 10 minutes
- "Tack‑free": 2 hours
- Minimum intercoat drying: 5 minutes
- Temperature drying:
- +60 °C: 30 minutes
Complete film formation: 7 days under natural drying.
Data are given at 65% relative humidity. Values may change with humidity variations.